Alkyd resin

Get A Quote

Model	Hydroxyl value mgKOH/g	viscosity mPa·s/25℃	Contained %	Acid value mgKOH/g	Characteristics and uses
JS128-70	130±10	40000-60000	70±2	≤10	It is a hydroxyl-type polyurethane alkyd resin with light color. When matched with PU curing agent, it has fast drying speed, high gloss and good fullness. ① Combined with PU curing agent, it can be made into two-component PU bright varnish, bright colored paint, yellowing resistant/semi-matt varnish. ②Can also be used for curing coatings, amino coatings, etc.
JS303-70	120±10	50000-80000	70±2	≤10	It is a hydroxyl-type polyurethane alkyd resin with moderate performance, fresh and low-odor paint film, and is suitable for general use on bottom surfaces. Good economy ① When combined with PU curing agent, it can be made into two-component PU primer and topcoat; ② It can also be used for curing coatings, amino coatings, etc.
JS3670	100±10	40000-60000	70±2	≤16	It is a hydroxyl-type polyurethane alkyd resin. When used with PU curing agent, it dries quickly and has good toughness. The primer is easy to polish and the topcoat is easy to matte; medium value, 1. When combined with PU curing agent, it can be made into two-component PU primer and topcoat; 2. It can also be used for curing coatings, amino coatings, etc.
JS342-70	140±10	30000-50000	70±2	≤12	It is a hydroxyl-type polyurethane alkyd resin and is matched with PU curing agent. It dries quickly and the paint film is fresh and odorless after drying. It has good toughness, high transparency and good fullness. Application areas: 1. Combined with PU curing agent, it can be made into a high-surface, fresh and odorless topcoat; 2. It can also be used for curing coatings, amino coatings, etc.
JS-01	170±10	30000-50000	65±2	≤12	Comparable to PU curing agent, it has moderate drying speed, high gloss and good fullness. Suitable for high-end base and topcoat, no foundation and low powder content, good filling properties, thick coating is not easy to cause prickly heat, does not sink, and does not cause pinholes. Application areas: 1. Combined with PU curing agent, it can be made into high-quality two-component PU primer and topcoat;
JS380-70	185±10	2000~3500	65±2	≤15	Suitable for two-component high-grade topcoat, fast drying, easy matting, good compatibility with vulcanized cotton, and low odor. Application fields: 1. Combined with PU curing agent, it can be made into high-quality two-component PU primer and topcoat;
JS301-70	125±10	10000~20000	65±2	≤10	The hydroxyl-type polyurethane alkyd resin has a high hydroxyl value, good solvent release, and is suitable for thick coating. The coating film is fresh and odorless, has high hardness, excellent transparency, and good fullness. Application areas: 1. Combined with PU curing agent, it can be made into two-component PU primer and topcoat; 2. Nitrocellulose paint.
JS301-70A	122±10	40000~60000	70±2	≤12	It is a hydroxyl-type polyurethane alkyd resin and is matched with PU curing agent. It has moderate drying speed, high gloss and good fullness. Application areas: 1. Combined with PU curing agent, it can be made into two-component PU primer and topcoat; 2. Nitrocellulose paint.
JS301-70G	122±10	80000~100000	70±2	≤12	It is a hydroxyl-type polyurethane alkyd resin and is matched with PU curing agent. It has moderate drying speed, high gloss and good fullness. Application areas: 1. Combined with PU curing agent, it can be made into two-component PU primer and topcoat;
JS3660	100±10	20000~30000	60~64	≤15	It is a hydroxyl-type polyurethane alkyd resin. It is matched with PU curing agent. It has fast drying speed and good toughness. The primer is easy to polish and the topcoat is easy to matte. Medium value. Application fields: 1. Combined with PU curing agent, it can be made into two-component PU primer and topcoat; 2. It can also be used in acid-cured coatings, amino coatings, etc.
JS301-65	125±10	10000~20000	63~67	≤10	The hydroxyl-type polyurethane alkyd resin has a high hydroxyl value, good solvent release, and is suitable for thick coating. The coating film is fresh and odorless, has high hardness, excellent transparency, and good fullness. Application areas: 1. Combined with PU curing agent, it can be made into two-component PU primer and topcoat; 2. Nitrocellulose paint.
JS302-70	120±10	80000~100000	68~72	≤12	It is a hydroxyl-type polyurethane alkyd resin with moderate performance, light color and low viscosity. When paired with PU curing agent, it has fast drying speed, high gloss, good fullness and good hardness. Application fields: 1. Combined with PU curing agent, it can be made into two-component PU primer and topcoat; 2. It can also be used in acid-cured coatings, amino coatings, etc.
JS304-70	155±10	8000~18000	68~72	≤12	It is a hydroxyl-type polyurethane alkyd resin with light color, low viscosity and excellent instant leveling. It has good solvent release and is suitable for thick coating. The coating film is fresh and odorless, has high hardness, good toughness, excellent transparency and good fullness. Application fields: 1. Combined with PU curing agent, it can be made into high-quality two-component PU primer and topcoat; 2. It can also be used in acid-cured coatings, amino coatings, etc.
JS3880	155±20	22000~28000	72~76	≤9	Very reactive and compatible alkyd resin, primer, high film hardness, good fullness, PU matte finish, scratch resistance, dry feel, high-end two-component PU system especially recommended for wood. Application fields: Suitable for PU varnish, including matte varnish and colored paint.
JS3970	155±10	8000~18000	68~72	≤12	It is a hydroxyl-type polyurethane alkyd resin with light color, low viscosity and excellent instant leveling. It has good solvent release and is suitable for thick coating. The coating film is fresh and odorless, has high hardness, good toughness, excellent transparency and good fullness. Application fields: 1. Combined with PU curing agent, it can be made into high-quality two-component PU primer and topcoat; 2. It can also be used in acid-cured coatings, amino coatings, etc.
JS382-65	140±10	8000~18000	65±2	≤12	Matched with PU curing agent, it has moderate drying speed, high gloss and good fullness. Suitable for high-end base and topcoat, no foundation and low powder content, good filling properties, thick coating is not easy to cause prickly heat, does not sink, and does not cause pinholes. Application fields: In combination with PU curing agent, it can be made into high-quality two-component PU primer and topcoat;
JS126-70 water white	120±10	10000~20000	68~72	≤12	It is a short-oil alkyd resin with hydroxyl groups, light color and low viscosity. When paired with PU curing agent, it has fast drying speed, high gloss, good fullness and excellent hardness. Application fields: When matched with PU curing agent, it can be used to make high-quality two-component PU glossy clear and glossy colored paint; it can be used to make glossy white surfaces, retaining gloss and color, and resisting yellowing.
JS127	140±10	25000~35000	68~72	≤10	It is a short-oil alkyd resin with hydroxyl groups. It has light color and is matched with PU curing agent. It has a moderate drying speed and is matched with curing agent. It has high hardness and excellent fullness. It has high gloss and good fullness. Application fields: 1. When matched with PU curing agent, it can be made into two-component PU glossy clear, glossy colored paint, etc. 2. It can also be used for acid-cured coatings, amino coatings, etc.
JS352	160±10	25000~40000	78~82	≤15	It is a short oil alkyd resin with hydroxyl group, high solid and low viscosity, light color, combined with curing agent, high hardness and excellent fullness. Application fields: 1. Added to PU main paint, it can significantly improve the fullness; 2. It can be made into PU clear topcoat and white topcoat separately, with good gloss and color retention and resistance to yellowing; 3. It can also be used in acid-cured coatings, amino coatings, etc.
JS353	180±10	40000~60000	78~82	≤15	It is a short oil alkyd resin with hydroxyl group, high solid and low viscosity, light color, combined with curing agent, high hardness and excellent fullness. Application fields: 1. Added to PU main paint, it can significantly improve the fullness; 2. It can be made into PU clear topcoat and white topcoat separately, with good gloss and color retention and resistance to yellowing; 3. It can also be used in acid-cured coatings, amino coatings, etc.
JS355	180±10	35000~55000	78~82	≤15	It is a short oil alkyd resin with hydroxyl group, high solid and low viscosity, light color, combined with curing agent, high hardness, excellent fullness, good economy, and slightly slow drying. Application fields: 1. Added to PU main paint, it can significantly improve the fullness; 2. It can be made into PU clear topcoat and white topcoat separately, with good gloss and color retention and resistance to yellowing; 3. It can also be used in acid-cured coatings, amino coatings, etc. 4. Curing agent intermediate.
JS356	140±10	25000~35000	78~82	≤10	It is a short-oil alkyd resin with hydroxyl groups, high solids and low viscosity, light color, combined with curing agent, high hardness, excellent fullness, good economy, and slightly slow drying. Application fields: 1. Added to PU main paint, it can significantly improve the fullness; 2. It can be made into PU clear topcoat and white topcoat separately, with good gloss and color retention and resistance to yellowing; 3. It can also be used in acid-cured coatings, amino coatings, etc. 4. Curing agent intermediate.

Products Inquiry

Submit

Get A Quote

Whatsapp: +86-13925274859

Email: zg99@puyangjingsen.com

Phone: +86-13925274859

Office Address:
A12-602, Low-Carbon Headquarters Park, 400 Xincheng Avenue, Zengcheng District, Guangzhou
Northern Plant Address:
Jinpu Road, Puyang Industrial Park, Puyang City, Henan Province

Product Series

Resin Series

Water-Based Material Series

Curing Agent Series

UV Coating Resin Series

Company